Wear resistant coating

Bruchure: Martec Nano Seal

Wear protective coatings Martec Nederland.

Martec Nano Seal. Martec Nano Seal. For revision and preservation of machine parts Martec Nederland features the possibillity to apply wear protective coatings. Martec Nano Seal offers a solution for extreme wear protection and hard to tamper base materials and shapes. By applying a 3 component composite system special properties are created. The composition can be adapted to a specific wear image. Martec Nano Seal can be used for preservation and repairing wear parts.

Application's Martec Nano Seal.

Extreme wear Erosion Heavy fibrations Pitting corrosion Cavitation Thermoshock Emergency repairs

Pitting Electrolytical degredation Chemical degredation Fouling, microbiological accretion, calcification Strength corrosion Suture, fixation and repair of machine parts

Application area's and product's Martec Nano seal.

Paper industry Pumps Chemical industry Ceramic and brick industry Waste treatment / recycling

Biogass industry, composting plants Cement and concrete industry Power plants Sugar industry Machine construction

Types and properties: Extreme wear resistant, spherical parts

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B1	Gray-white 3:1	80 ℃ 150℃	2,60	85-90	35 N/mm2 90 N/mm2	Extreme wear High strength ceramical particles up to 1,5 mm.
MNS B1+	Gray-white 3:1	80℃ 150℃	2,60	85-90	35 N/mm2 90 N/mm2	As B1 but with higher chip-off resistance hogere( < 1cm layer possible)
MNS B1 EE	Gray-white 1:2,3	60℃ 90℃	2,20	40-70 1)	16 N/mm2	As B1 But higher impact resistance
MNS  B1 GF	Gray-white 3:1	60℃ 90℃	2,30	85-90	40 N/mm2 90 N/mm2	As in B1 but with glassfiber reinforcement  with flexible hardner outside coating for ducts and suitable for fibrations
MNS B1 F	Gray-white 1,75:1	60℃ 90℃	2,00	82-87	18 N/mm2 60 N/mm2	As B1 S but with extreme fast hardning
MNS B1 M	Gray-white 3:1	80℃ 150℃	2,60	85-90	35 N/mm2 90 N/mm2	As B1 but with bigger particles up to 2mm.
MNS B1 S	Gray-white 3:1	80℃ 150℃	2,50	85-95	37 N/mm2 95 N/mm2	As B1 but with smaller particles up to 0,5 mm.

Chemical resistance

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B3	Gray-brown 2:1	80 ℃ 175℃	1,30	80-82	25 N/mm2 65 N/mm2	Extreme protection against agressive chemicals
MNS B3 TF	Grijs	110℃ 180℃	1,40	80-84	23 N/mm2	Protection for metals against extreme chemicals and corrosion

Wear protection, Erosion, Corrosion, fine small sharp ceramical particles

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B4	Dark gray 5:1	60 ℃ 100℃	1,70	80-85	27 N/mm2 82 N/mm2	Good wear resistance against fluid abrasion. Very elastic, Good fixation, Tuv approval for use in nucleair power plants
MNS B4+	Dark gray	80℃ 160℃	1,70	87-89	38 N/mm2 93 N/mm2	less fluid in appliance as B4
MNS B4 KF	Dark gray 5:1	80℃ 160℃	1,65	74-78	24 N/mm2 68 N/mm2	As B4 but better resistance to thermoshock and low temperature, Anti-slip layers in cooled ware houses
MNS B4 AS	Gray 5:1	40℃ -30℃  +80℃	1,50	72-78	27 N/mm2 82 N/mm2	As B4 But antistatic, low surface resistance
MNS B4 LM	Gray 3:1	80℃ 100℃	1,80	80-82	26 N/mm2 74 N/mm2	As B4 But with food approval up to 70℃ (condensing test ISO 6270), extreme resistance to chemical wear
MNS B4 NV	Gray 4,6:1	70℃ 110℃	1,70	80-85	27 N/mm2 82 N/mm2	As B4 But with low viscosity for appliance and best resistance to chemicals, very good results in acid tests
MNS B4 EE	Gray 0,607:1	45℃ 80℃	1,20	40	14 N/mm2	As B4 But extreme elastic
MNS B4 TF	Gray 8:1	80℃ 140℃	1,70	80-85	27 N/mm2 82 N/mm2	As B4 But resistant to high temperatures
MNS B4 NF SF	Gray 3,1:1	45℃ 80℃	1,50	70-75	21 N/mm2	As B4 But high impact strength and wear resistance

Anti stick.

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B4 AH-7	White 6,5:1	45 ℃ 80℃	1,60	80-85		Wear resistant with anti stick properties
MNS B4 AH	White 6,5:1	30℃ 40℃	1,50	87-89		Extreme anti stick properties and mild wear resistance
MNS B3 AH-7	White - Gray	50℃ 90℃	1,4	74-78		Good anti stick properties and wear resistance,less ceramic as B4 AH-7 and smoother surface

Corrosion, Erosion.

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B5	Gray brown 2:1	60 ℃ 170℃	1,40	83-86	35 N/mm2 70 N/mm2	Small ceramic particles but less then B4. Against all forms off light corrosion and erosion.

Preserving machine parts.

Martec Nano Seal	Color Comp. A:B	Temperature Wet : Dry	Weight g/cm3	Hardness Shore D	Tensile strength Pressure strength	Application area's
MNS B6	Gray  5:1	80 ℃ 160℃	2,20	85-88	31 N/mm2 89 N/mm2	Machinable with high chipp off resistance. Rebuilding worn metal parts.
MNS K14		60 ℃ 80℃	1,60	80-85	27 N/mm2 82 N/mm2	Very wer resistant filler for machine building. Very high fix on Fe + Alu. Hole filler, fixating and adjusting machine parts instead of complexe machining.